ABAZONE-290

SOLVENT FREE TWO CPMPONENTS EPOXY OFFSHORE SPLASHZONE COATING

DESCRIPTION

ABAZONE-290 is a two components, solvent free, high solids, modified epoxy coat designed to give long term protection in a single coat application for offshore splash zone application. It will continue to cure when immersed in water and due to epoxy modification, it is suitable to use in exterior area.

SURFACE PREPARATION

Concrete

All surfaces should be clean, dry and free from curing compounds, release agents, troweling compounds, standing water, grease, oil, dirt, bitumen coatings and loose or disintegrating concrete. All poured and precast concrete must also have blasted, wire brushed or acid etched to remove laitance.

Surface preparation shall not take place in following conditions:

  • At temperature below 5 ºC.
  • When the surface temperature is less than 3 ºC above the dew point.

 

APPLICATION

Material is supplied in two containers as a unit. Always mix a complete unit in the proportion supplied. Once the unit has been mixed it must be used within the working Pot life specified. 

1-Agitate Part A and B separately with a power agitator.                                                             

2-Combine entire contents of curing agent (part B) with base (part A) and mix thoroughly with power agitator.

3-Mix thoroughly for at least three minutes, scraping the container bottom and side to assure    complete mixing. There is no induction or waiting time required after mixing before application.

ABAZONE-290 coating can be applied using good quality rollers or short haired brushes or by airless spray. It is recommended that ABAZONE-290 coating be applied in two coats to ensure complete coverage. Prior to the application of each coat the surface should be examined for signs of pin-holing, etc. Where pin-holing is evident these should be filled using ABADUR MP repair system.

If the over-coating is delayed more than the drying time table, the previous coat must be thoroughly abraded to give an adequate mechanical key and solvent wiped. In hot climate, material temperature should be 20 to 25 ºC prior to mixing; otherwise pot life becomes very short. Do not thin for any reason.

 

  • Excellent adhesion to wet and dry substrates.
  • UV resistance.
  • Ability to cure under water.
  • Excellent resistance to chloride and seawater.
  • Good weathering resistance.
  • Easy to apply.
  • Solvent-free .

  • Offshore splash zone concrete maintenance.
  • Offshore splash zone structure of docks.

TECHNICAL PROPERTIES

Color

Light grey

Mixing Ratio

3:1(by weight)

Density (A+B)

Approx. 1.4 g/cm3

Volume solid

100%

Coverage

0.4-0.8kg/m²/coat, two coats are recommended

Typical dry film thickness

250-500 microns

Number of coats

Two

Application method

Roller, brush or airless spray

Substrate

Concrete

Flash point

80°C

Cleaner

T-200

 

Drying Time

Full cure

Over-coating

Touch dry

Temperature

Max

Min

13 days

3 days

32 hrs

9 hrs

15°C

7 days

2 days

24 hrs

6 hrs

25°C

4 days

1 days

18 hrs

4 hrs

40°C

 

Pot Life

40°C

25°C

15°C

Material temperature

20 min

45 min

70 min

Pot life

.

  • Shelf life: 12 months in unopened original package.
  • Storage condition: should be protected from frost, direct sunlight and moisture. Keep in the temperature range between +10°C and +30°C.
  • Packing: Pre-batched Part A: 10.5 kg & Part B: 3.5 kg units, 14 kg at Total.

 

For information and advice on the safe handling, storage and disposal of chemical products, users   shall refer to the most recent Material Safety Data Sheet (available on request) containing physical, ecological, toxicological and other safety-related data.

WE DEVELOP CHEMISTRY